Dental Lab 1200 MPa 1200HV 1530℃ Dental Zirconia Disc
Product Details
| Name: | 1530℃ Dental Zirconia Disc | Hardness: | 1200HV |
|---|---|---|---|
| Sintering Temperature: | 1530 ℃ | Strength: | 1200 MPa |
| Instrument Classification: | Class II | Sample: | Offer |
| Package: | OEM (dental Material) | Application: | Dental Areal, Dental Lab |
| Thickness: | 10/12/14/16/18/20/22/25mm | Size: | 98x10/12/14/16/18/20/22/25 |
| Diameter: | 98mm | System: | Open/zirkonzahn/Amann/Sirona |
| Warranty: | 5 Year | Shape: | Disc |
| Highlight |
1200 MPa Dental Zirconia Disc,1200HV Dental Zirconia Disc,1530℃ Dental Zirconia Disc |
||
Product Description
Open system Dental Zirconia HT High Strength Zirocnia Block for Coping
Dental Zirconia Disc
To achieve expected quality, the sintering curves must be followed.
Note: please employ high-temperature furnace specially designed for denture manufacturing. It is good for ceramics sintering to prolong heating up time and cooling time properly.
1. Sintering preparation: Make sure there is enough sintering space to avoid deformation. After dyeing, the restoration must be dried. Do not heat up too quickly for it might result in cracks. Make sure the dust-proof cover is put on the crucible to keep impurity away from restorations
2. After sintering: Following the instruction to lower temperature and take out restorations. Do not reduce furnace temperature too quickly to avoid cracks.
3.The highest temperature: the highest temperature will affect the translucency and dyeing results. Make sure the accurate temperature of every step. Sinter and preserve heat according to the instruction.
High Translucency Dental Zirconia Disc For Anterior Restorarion , Dental Zirconia Blank
YUCERA blanks are made from biocompatible zirconiumdioxyde. The yttrium oxide stabilizing protects the material against cracks and increases the tensile and compressive strength. The special grain size allocation inside the material and the added aluminium oxide also result in extra strength during milling and subsequently in clinical use. The outstanding mechanical characteristics, excellent chemical durability and the unbeaten biocompatibility combined with the translucent color predestine XTCERA as the ideal material provider for dental milling systems.
YUCERA HT translucency, apply to single crown, anterior teeth, inlay/onlay and also veneers.
HT Dental Zirconia Disc
* High translucent
* Brilliant bending strength and economic block
* Suitable for coping and framework
Indications
Coping, Inlay, Onlay, Bridge, Crown
Physical Characteristics
|
Physical Characteristics |
|
Sintered density 6.07±0.01g/cm³ |
|
Bending Strength 1200 MPa |
|
Transmittance 41% |
|
Hardness 1200HV |
|
Sintering temperature 1480~1550℃/recommend 1530℃ |
Product Highlights
Open system Dental Zirconia HT High Strength Zirocnia Block for Coping Dental Zirconia Disc To achieve expected quality, the sintering curves must be followed. Note: please employ high-temperature furnace specially designed for denture manufacturing. It is good for ceramics sintering to prolong heating up time and cooling time properly. 1. Sintering preparation: Make sure there is enough sintering space to avoid deformation. After dyeing, the restoration must be dried. Do not
49% Translucent 3D Plus Multilayer 16 color Zirconium Blocks
Yucera zirconia block 3D Plus multilayer 16color zirconia blocks Super Translucent Advantages 1, Excellent translucency 2, High flexural strength 3,Accurate shading when working with our color liquid 4, Good machinability 5, Extremely safe Pre-shaded zirconia block Advantages - 16 A-D shades available; - High translucency(43-57% % total light transmittance) - High flexural strength - accurate, even and stable color; - No hand coloring needed Zirconia Block Introduction Yucera
Yucera Lightweight Dental 3D Printer Anti Aliasing With 57 Stepper Motor
Yucera dental lab new type 3D printer high speed manufacturer price Hot sale dental printer Detailed Product Description of dental 3D printer: Drive motor:57 stepper motor Connection method: USB, WIFI Safety standards: UL/FCC/CE/ROHS/PSE Printing size:192*120*100mm XY axis accuracy:0.05mm Print speed:1-4s/layer,30mm/h Print layer thickness:0.025-0.1mm Anti-aliasing:8times anti-aliasing Support consumable types:405nm wavelength photosensitive resin, compatible with third-party
CAD CAM Dental Sintering Furnace 1200C For Lithium Disilicate Ingots
Dental Equipment for dental lab press lithium disilicate ingots using Dental Lithium HT/LT dental press inogots furnace Detailed Product Description of dental sintering furnace: Detailed Product Description of dental furnace: itemvalue / Rated power 1500W Model Number oP6010 Waranty 1Year After-sale Service|online technical support online technical support Material metal,plastic Place of Origin China Shelf Life of dental press inogots furnace:3 years Quality certification of
Yucera Dental Laboratory Zirconia Sintering Furnace F10+ With 40C/min Heating Rate
Advantage for Yucera F10+ Sintering Dental Furance 1.Touch screen operation is more convenient 2.High-performance thermal insulation material, long-lasting thermal insulation, safe and pollution-free 3.Built-in automatic cooling program, precise temperature control 4.WiFi networking, remote monitoring 5.PID intelligent temperature ,wrap-around heating, uniform sintering Character for Sintering Dental Furance * This 1560℃ Dental zriconia sintering furnace is perfectly suited
Please use our online inquiry contact form below if you have any questions, our team will get back to you as soon as possible.