| MOQ: | Negotiation |
| Price: | Negotiation |
| Standard Packaging: | 45*21*25 cm 30pcs/carton |
| Delivery Period: | 5-8 working days |
| Payment Method: | T/T, Western Union |
| Supply Capacity: | 20000 pieces per month |
YUCERA Dental Materials And Equipment Manufacturer Economical Dental Zirconia Blanks For Dental Laboratory
To achieve expected quality, the sintering curves must be followed.
Note: please employ high-temperature furnace specially designed for denture manufacturing. It is good for ceramics sintering to prolong heating up time and cooling time properly.
1. Sintering preparation: Make sure there is enough sintering space to avoid deformation. After dyeing, the restoration must be dried. Do not heat up too quickly for it might result in cracks. Make sure the dust-proof cover is put on the crucible to keep impurity away from restorations
2. After sintering: Following the instruction to lower temperature and take out restorations. Do not reduce furnace temperature too quickly to avoid cracks.
3.The highest temperature: the highest temperature will affect the translucency and dyeing results. Make sure the accurate temperature of every step. Sinter and preserve heat according to the instruction.
Zirconia Block Introduction
Yucera zirconia block has high strength, excellent permeability and color aesthetic repair effect that suitable for CAD/CAM system and manual system.
Product Features
Safety:No irritation,No corrosion,Good bio-compatibility
Beauty:Natural teeth color can be reproduced
Comfortability:Low thermal conductivity,hot and cold changes do not stimulte the pulp
Durability:Over 1600MPa perturbed strength, durable and useful
HT Zirconia Block
*High translucent
*Brilliant bending strength and economic block
*Suitable for coping and framework
Indications
Coping, Inlay, Onlay, Bridge, Crown
Physical Characteristics
| Physical Characteristics |
| Sintered density 6.07±0.01g/cm³ |
| Bending Strength 1200 MPa |
| Transmittance 41% |
| Hardness 1200HV |
|
Sintering temperature 1480~1550℃/recommend 1530℃ |
Video
Video
Video
Video
|
|
| MOQ: | Negotiation |
| Price: | Negotiation |
| Standard Packaging: | 45*21*25 cm 30pcs/carton |
| Delivery Period: | 5-8 working days |
| Payment Method: | T/T, Western Union |
| Supply Capacity: | 20000 pieces per month |
YUCERA Dental Materials And Equipment Manufacturer Economical Dental Zirconia Blanks For Dental Laboratory
To achieve expected quality, the sintering curves must be followed.
Note: please employ high-temperature furnace specially designed for denture manufacturing. It is good for ceramics sintering to prolong heating up time and cooling time properly.
1. Sintering preparation: Make sure there is enough sintering space to avoid deformation. After dyeing, the restoration must be dried. Do not heat up too quickly for it might result in cracks. Make sure the dust-proof cover is put on the crucible to keep impurity away from restorations
2. After sintering: Following the instruction to lower temperature and take out restorations. Do not reduce furnace temperature too quickly to avoid cracks.
3.The highest temperature: the highest temperature will affect the translucency and dyeing results. Make sure the accurate temperature of every step. Sinter and preserve heat according to the instruction.
Zirconia Block Introduction
Yucera zirconia block has high strength, excellent permeability and color aesthetic repair effect that suitable for CAD/CAM system and manual system.
Product Features
Safety:No irritation,No corrosion,Good bio-compatibility
Beauty:Natural teeth color can be reproduced
Comfortability:Low thermal conductivity,hot and cold changes do not stimulte the pulp
Durability:Over 1600MPa perturbed strength, durable and useful
HT Zirconia Block
*High translucent
*Brilliant bending strength and economic block
*Suitable for coping and framework
Indications
Coping, Inlay, Onlay, Bridge, Crown
Physical Characteristics
| Physical Characteristics |
| Sintered density 6.07±0.01g/cm³ |
| Bending Strength 1200 MPa |
| Transmittance 41% |
| Hardness 1200HV |
|
Sintering temperature 1480~1550℃/recommend 1530℃ |