Three Point Bending Strength: | 400±60Mpa | Sintering Temperature:: | 450-840℃ |
---|---|---|---|
Translucency:: | 48% | Size: | 18*13*15mm |
Color: | VITA16, Bleach White 4 (BL1/BL2/BL3/BL4) | Indication: | Coping /Inlay /Onlay /Anterior/Veneer |
Advantage: | Natural Esthetics And Efficient Process | Usage: | PROFESSIONAL DENTAL, Orthodontic Dental Teeth, Denture Teeth, Anterior Teeth, Coping;crown;bridge |
Density[g/cm3: | 2.47±0.05 | Chemical Solubility [μg/cm2: | ≤40 |
Coefficient Of Thermal Expansion (25-500℃)[10-6/K: | 10.5±0.5 | Transparency: | LT (low Transparency)/HT(high Transparency) |
High Light: | C14 Lithium Disilicate Ceramic,VITA16 Lithium Disilicate Ceramic,Lithium Disilicate Ceramic Blocks |
VITA16 Ceradirect Lithium Disilicate Ceramic Blocks C14 HT LT For Dental Lab
Ceradirect Lithium dislicate blocks(Glass Ceramic)-C14-HT/LT(5 pieces)—for dental lab CAD/CAM Lithium dislicate blocks
Features for lithium dislicate/ glass ceramic block:
E.max IPS glass ceramics, the main component is lithium disilicate, which is made by special technology. because It has a simple, fast crystallization process and an ultra-high aesthetic restoration effect, and becomes a CAD The choice of materials for high efficiency and high strength repair.
1. Globally popular digital chair side all-ceramic material;
2. Easy to mill and crystallization process only takes 20 minutes;
3. CAD/CAM system of high efficiency;
4. Precise production process precisely matched, advanced to achieve instant restoration;
5. Superior transparency, presenting a highly bionic aesthetic effect.
[Main ingredient] :
Composition |
Percentage |
SiO2 |
55%~65% |
Li2O |
15%~25% |
Al2O3 |
2%~12% |
K2O |
2%~12% |
Other |
0%~10% |
complement:
Coefficient of thermal expansion |
Three point bending strength[MPa] |
Chemical solubility |
Density[g/cm3] |
10.5±0.5 |
400±60 |
≤40 |
2.47±0.05 |
calcining curve:
The initial |
The drying time |
Heating rate |
The highest |
The highest |
The final |
450℃ |
4min |
40℃/min |
840℃ |
6min or 2min |
300℃ |
Product advantages:
1. Excellent mechanical strength: The three-point bending strength is increased to 400±60 MPa, allowing CAD/CAM system to design with higher accuracy, reducing the processing difficulty of ultra-thin veneer and other restorations, and improving the strength and safety of materials seated in the Mouth;
2. Overall fitness , easy to seat: The scientific nanosmicron crystallization structure provides better edge stability and structural accuracy for milling restoration, effectively simplifies the operation process of repeated seating and polishing, and realizes the efficient fitting of the technician's processing and clinical seating teeth;
3.The clinical experience of instant restoration: As an all-ceramic material with a shrinkage ratio close to zero, it can provide great convenience for efficient design and digital processing, and provide you with ideal and comfortable instant diagnosis and treatment experience combined with the rapid crystallization process;
Colors
A1, A2, A3, A3.5, A4; |
B1, B2, B3, B4; |
C1, C2, C3, C4; |
D2, D3, D4; |
BL1, BL2, BL3, BL4 |
Packaging
5 pieces in a box
YUCERA Dental Glass Ceramic all series
Thickness(mm) | HT (high transparency) |
LT (low transparency) |
Item |
18*13*15 | A1,A2,A3,A3.5,A4 B1,B2,B3,B4 C1,C2,C3,C4 D2,D3,D4 BL1,BL2,BL3,BL4 |
A1,A2,A3,A3.5,A4 B1,B2,B3,B4 C1,C2,C3,C4 D2,D3,D4 BL1,BL2,BL3,BL4 |
C14 |
40*15*14 | A1,A2,A3,A3.5,A4 B1,B2,B3,B4 C1,C2,C3,C4 D2,D3,D4 BL1,BL2,BL3,BL4 |
A1,A2,A3,A3.5,A4 B1,B2,B3,B4 C1,C2,C3,C4 D2,D3,D4 BL1,BL2,BL3,BL4 |
B40 |
Suitable for Sirona, Roland, Imes-icore machine.
Package:
Factory and team members:
Recommend product:
Features for lithium dislicate/ glass ceramic block: