CAD CAM Dental Zirconia Blank
Advantages :
- Top raw material from Tosoh in Japan
- 16 A-D shades available;
- High translucency(41% total light transmittance)
- High flexural strength
- accurate, even and stable color;
- No hand coloring needed
CAD CAM Dental Zirconia Blank High density and strength
(1) The strength is 1.5 times higher than the second generation of EMPRESS.
(2) The strength is more than 60% higher than INCERAM alumina.
(3) Unique crack resistance and tough curing performance after cracking.
(4) Porcelain bridges with more than 6 units can be made, which solves the problem that all-ceramic systems cannot be used as long bridges.
CAD CAM Dental Zirconia Blank Feature
high flexural strength, fracture resistance, exceptional durability, and easy milling properties with precision. Pre-shaded zirconia disc consisting of three pre-colored layers Easy Handling: Polish or Glaze after Sintering Ideal for full contour crowns and bridges
CAD CAM Dental Zirconia Blank Introduction
Yurucheng zirconia block has high strength, excellent permeability and color aesthetic repair effect that suitable for CAD/CAM system and manual system.
Safety:No irritation,No corrosion,Good bio-compatibility
Beauty:Natural teeth color can be reproduced
Comfortability:Low thermal conductivity,hot and cold changes do not stimulte the pulp
Durability:Over 1600MPa perturbed strength, durable and useful
CAD CAM Dental Zirconia Blank
* Pre-shaded technics
* Uniform color
* Without post dyeing posses
* Suitable for full contour crown, bridge and anterior
Indications
Crown, Inlay, Onlay, 2-5 unit Bridges, Anterior
Physical Characteristics
Physical Characteristics |
Sintered density 6.07±0.01g/cm³ |
Bending Strength 1100 MPa |
Transmittance 45% |
Hardness 1200HV |
Sintering temperature 1480~1550℃/recommend 1530℃ |
HT/ST Sintering Curve (1-5)
| HT/ST Sintering Curve (1-5) | ||||
| Sintering step | Start Temperature(℃) | End Temperature(℃) | Time(Min) | Rate(℃/Min) |
| Step 1 | 20 | 300 | 30 | 9.3 |
| Step 2 | 300 | 1200 | 150 | 6 |
| Step 3 | 1200 | 1530 | 110 | 3 |
| Step 4 | 1530 | 1530 | 120 | 0 |
| Step 5 | 1530 | 800 | 100 | -7.3 |
| Step 6 | 800 | natural cooling 20 | 120 | -6.5 |
HT/ST Sintering Curve (10 units)
| HT/ST Sintering Curve (10 units) | ||||
| Sintering step | Start Temperature(℃) | End Temperature(℃) | Time(Min) | Rate(℃/Min) |
| Step 1 | 20 | 300 | 30 | 9.3 |
| Step 2 | 300 | 1200 | 190 | 4.7 |
| Step 3 | 1200 | 1530 | 150 | 2.2 |
| Step 4 | 1530 | 1530 | 120 | 0 |
| Step 5 | 1530 | 800 | 120 | -6 |
| Step 6 | 800 | natural cooling 20 | 120 | -6.5 |
Video
Video
Video
Video
Video
|
|
| MOQ: | Negotiation |
| Price: | Negotiation |
| Standard Packaging: | 45*31*25 cm , 30pieces/carton |
| Delivery Period: | 5-8 work days |
| Payment Method: | T/T, Western Union |
| Supply Capacity: | 20000 pieces per month |
CAD CAM Dental Zirconia Blank
Advantages :
- Top raw material from Tosoh in Japan
- 16 A-D shades available;
- High translucency(41% total light transmittance)
- High flexural strength
- accurate, even and stable color;
- No hand coloring needed
CAD CAM Dental Zirconia Blank High density and strength
(1) The strength is 1.5 times higher than the second generation of EMPRESS.
(2) The strength is more than 60% higher than INCERAM alumina.
(3) Unique crack resistance and tough curing performance after cracking.
(4) Porcelain bridges with more than 6 units can be made, which solves the problem that all-ceramic systems cannot be used as long bridges.
CAD CAM Dental Zirconia Blank Feature
high flexural strength, fracture resistance, exceptional durability, and easy milling properties with precision. Pre-shaded zirconia disc consisting of three pre-colored layers Easy Handling: Polish or Glaze after Sintering Ideal for full contour crowns and bridges
CAD CAM Dental Zirconia Blank Introduction
Yurucheng zirconia block has high strength, excellent permeability and color aesthetic repair effect that suitable for CAD/CAM system and manual system.
Safety:No irritation,No corrosion,Good bio-compatibility
Beauty:Natural teeth color can be reproduced
Comfortability:Low thermal conductivity,hot and cold changes do not stimulte the pulp
Durability:Over 1600MPa perturbed strength, durable and useful
CAD CAM Dental Zirconia Blank
* Pre-shaded technics
* Uniform color
* Without post dyeing posses
* Suitable for full contour crown, bridge and anterior
Indications
Crown, Inlay, Onlay, 2-5 unit Bridges, Anterior
Physical Characteristics
Physical Characteristics |
Sintered density 6.07±0.01g/cm³ |
Bending Strength 1100 MPa |
Transmittance 45% |
Hardness 1200HV |
Sintering temperature 1480~1550℃/recommend 1530℃ |
HT/ST Sintering Curve (1-5)
| HT/ST Sintering Curve (1-5) | ||||
| Sintering step | Start Temperature(℃) | End Temperature(℃) | Time(Min) | Rate(℃/Min) |
| Step 1 | 20 | 300 | 30 | 9.3 |
| Step 2 | 300 | 1200 | 150 | 6 |
| Step 3 | 1200 | 1530 | 110 | 3 |
| Step 4 | 1530 | 1530 | 120 | 0 |
| Step 5 | 1530 | 800 | 100 | -7.3 |
| Step 6 | 800 | natural cooling 20 | 120 | -6.5 |
HT/ST Sintering Curve (10 units)
| HT/ST Sintering Curve (10 units) | ||||
| Sintering step | Start Temperature(℃) | End Temperature(℃) | Time(Min) | Rate(℃/Min) |
| Step 1 | 20 | 300 | 30 | 9.3 |
| Step 2 | 300 | 1200 | 190 | 4.7 |
| Step 3 | 1200 | 1530 | 150 | 2.2 |
| Step 4 | 1530 | 1530 | 120 | 0 |
| Step 5 | 1530 | 800 | 120 | -6 |
| Step 6 | 800 | natural cooling 20 | 120 | -6.5 |