Dental Lab 1200 MPa 1200HV 1530℃ Dental Zirconia Disc
Product Details
| Name: | 1530℃ Dental Zirconia Disc | Hardness: | 1200HV |
|---|---|---|---|
| Sintering Temperature: | 1530 ℃ | Strength: | 1200 MPa |
| Instrument Classification: | Class II | Sample: | Offer |
| Package: | OEM (dental Material) | Application: | Dental Areal, Dental Lab |
| Thickness: | 10/12/14/16/18/20/22/25mm | Size: | 98x10/12/14/16/18/20/22/25 |
| Diameter: | 98mm | System: | Open/zirkonzahn/Amann/Sirona |
| Warranty: | 5 Year | Shape: | Disc |
| Highlight |
1200 MPa Dental Zirconia Disc,1200HV Dental Zirconia Disc,1530℃ Dental Zirconia Disc |
||
Product Description
Open system Dental Zirconia HT High Strength Zirocnia Block for Coping
Dental Zirconia Disc
To achieve expected quality, the sintering curves must be followed.
Note: please employ high-temperature furnace specially designed for denture manufacturing. It is good for ceramics sintering to prolong heating up time and cooling time properly.
1. Sintering preparation: Make sure there is enough sintering space to avoid deformation. After dyeing, the restoration must be dried. Do not heat up too quickly for it might result in cracks. Make sure the dust-proof cover is put on the crucible to keep impurity away from restorations
2. After sintering: Following the instruction to lower temperature and take out restorations. Do not reduce furnace temperature too quickly to avoid cracks.
3.The highest temperature: the highest temperature will affect the translucency and dyeing results. Make sure the accurate temperature of every step. Sinter and preserve heat according to the instruction.
High Translucency Dental Zirconia Disc For Anterior Restorarion , Dental Zirconia Blank
YUCERA blanks are made from biocompatible zirconiumdioxyde. The yttrium oxide stabilizing protects the material against cracks and increases the tensile and compressive strength. The special grain size allocation inside the material and the added aluminium oxide also result in extra strength during milling and subsequently in clinical use. The outstanding mechanical characteristics, excellent chemical durability and the unbeaten biocompatibility combined with the translucent color predestine XTCERA as the ideal material provider for dental milling systems.
YUCERA HT translucency, apply to single crown, anterior teeth, inlay/onlay and also veneers.
HT Dental Zirconia Disc
* High translucent
* Brilliant bending strength and economic block
* Suitable for coping and framework
Indications
Coping, Inlay, Onlay, Bridge, Crown
Physical Characteristics
|
Physical Characteristics |
|
Sintered density 6.07±0.01g/cm³ |
|
Bending Strength 1200 MPa |
|
Transmittance 41% |
|
Hardness 1200HV |
|
Sintering temperature 1480~1550℃/recommend 1530℃ |
Product Highlights
Open system Dental Zirconia HT High Strength Zirocnia Block for Coping Dental Zirconia Disc To achieve expected quality, the sintering curves must be followed. Note: please employ high-temperature furnace specially designed for denture manufacturing. It is good for ceramics sintering to prolong ...
49% Translucent 3D Plus Multilayer 16 color Zirconium Blocks
Yucera zirconia block 3D Plus multilayer 16color zirconia blocks Super Translucent Advantages 1, Excellent translucency 2, High flexural strength 3,Accurate shading when working with our color liquid 4, Good machinability 5, Extremely safe Pre-shaded zirconia block Advantages - 16 A-D shades ...
CAD CAM Dental Sintering Furnace 1200C For Lithium Disilicate Ingots
Dental Equipment for dental lab press lithium disilicate ingots using Dental Lithium HT/LT dental press inogots furnace Detailed Product Description of dental sintering furnace: Detailed Product Description of dental furnace: itemvalue / Rated power 1500W Model Number oP6010 Waranty 1Year After-sale ...
Yucera Dental Laboratory Zirconia Sintering Furnace F10+ With 40C/min Heating Rate
Advantage for Yucera F10+ Sintering Dental Furance 1.Touch screen operation is more convenient 2.High-performance thermal insulation material, long-lasting thermal insulation, safe and pollution-free 3.Built-in automatic cooling program, precise temperature control 4.WiFi networking, remote ...
Yucera 3D Flash Multilayer Dental Zirconia Block with 700-1050MPA Bending Strength 57%-46% Transmittance and 16 Color Options
Yucera's 3D Flash Multilayer Zirconia Block offers exceptional durability (1050 MPA strength) and high transmittance (57%) for dental crowns. CE Certified Class II with 1-year warranty. Fast 40-minute sintering boosts lab efficiency. 16 color options available.
Please use our online inquiry contact form below if you have any questions, our team will get back to you as soon as possible.